MOLYKOTE 1000 Solid lubricant paste APPLICATIONS:

Molykote 1000 is Suitable for bolted joints that are subjected to high temperatures up to 650 Degrees Centigrade and to corrosive effects, and which, after assembling and the initial operation, have to be re-tightened or disconnected. In order to ensure constant pre-stressing forces, uniform and steady coefficients of friction of the lubricant are necessary.

Molykote 1000  is used successfully for cylinder head bolts, nozzle head screws of plastic injection molding machines, bolted joints in the chemical industry, and also for the tension rings of centrifuges.

MOLYKOTE 1000 Solid lubricant paste FEATURES:

Molykote 1000 Can be used over a wide range of temperature - 30 Degrees Centigrade to + 650 Degrees Centigrade , High load-carrying capacity, Enables non destructive dismantling. Even after long use at high temperatures Coefficient of friction unchanged in the area of oiled bolts, even after several bolt re-tightening and loosening processes, Good corrosion protection.

MOLYKOTE 1000 Solid lubricant paste COMPOSITION:

• Solid lubricants

• Thickner

• Powdered Metal

• Mineral Oil

MOLYKOTE 1000 TYPICAL PROPERTIES

Color : Brown

Penetration density : ISO 2137 Unworked penetration mm/10 280-310 &  ISO 2811 Density at 20°C (68T)

Temperature Resistance :

Service temperature1 °C -18 to 1093

Load-carrying capacity, wear protection, service life

Four-ball tester

• DIN 51 350 pt.4 Weld load N 4800

• DIN 51 350 pt.5 Wear scar under 400N load mm 0.08

Frictional force

• Coefficient of friction

• Screw test - u thread2 0.13

• Screw test - u head 0.08

• Initial break-away torque3 Nm 135